| 04.01
HARDENER 111 |
| Type |
: |
Aliphatic
Polyamine |
Viscosity
in Supply at
at 25°C in Cps. |
:
|
15
- 25 |
| Density
g/CM³ |
: |
0.98
- 0.99 |
| Amine
Value mg. KOH/g. |
: |
2250
Approx |
| Amine
eq. wt. |
: |
25
|
| Mixing
ratio with 100 parts of |
| SYNPOL
200 |
: |
10 - 14
|
| SYNPOL
450 XX |
: |
5 - 7
|
| Cure
conditions |
: |
16 - 24 hours at 250 |
| Notes |
: |
Electrical potting, encapsulation, casting,
hand lay-up lamination & tooling, flooring surfacing &
adhesives. Coal tar modified surface coatings.
|
|
| |
| 04.02
HARDENER 222 |
| Type |
: |
Aliphatic
Polyamine |
Viscosity
in Supply at
at 25°C in Cps. |
:
|
7
- 10 |
| Density
g/CM³ |
: |
0.95
- 0.96 |
| Amine
Value mg. KOH/g. |
: |
2650
Approx |
| Amine
eq. wt. |
: |
21
|
| Mixing
ratio with 100 parts of |
| SYNPOL
200 |
: |
8 - 12
|
| SYNPOL
450 XX |
: |
4 - 6
|
| Cure
conditions |
: |
16 - 24 hours at 250 |
| Notes |
: |
Electrical potting, encapsulation, casting,
hand lay-up lamination & tooling, flooring surfacing
& adhesives. Coal tar modified surface coatings.
|
|
| |
| 04.03
HARDENER 240 |
| Type |
: |
Modified
aliphatic polyamine |
Viscosity
in Supply at
at 25°C in Poises. |
:
|
2
- 5 |
| Density
g/CM³ |
: |
1.01
- 1.05 |
| Amine
Value mg. KOH/g. |
: |
725
- 800 |
| Amine
eq. wt. |
: |
40
|
| Mixing
ratio with 100 parts of |
| SYNPOL
200 |
: |
20 - 22
|
| SYNPOL
450 XX |
: |
--
|
| Cure
conditions |
: |
16 - 24 hours at 250 |
| Notes |
: |
Safe hardener for casting, potting,
lamination, tooling, adhesives with short pot
life & fast curing properties.
|
|
| |
| 04.04
HARDENER 260 |
| Type |
: |
Modified
aliphatic polyamine |
Viscosity
in Supply at
at 25°C in Cps. |
:
|
75
- 80 |
| Density
g/CM³ |
: |
1.0
- 1.1 |
| Amine
Value mg. KOH/g. |
: |
675
- 775 |
| Amine
eq. wt. |
: |
44
|
| Mixing
ratio with 100 parts of |
| SYNPOL
200 |
: |
22 - 24
|
| SYNPOL
450 XX |
: |
--
|
| Cure
conditions |
: |
16 - 24 hours at 250 |
| Notes |
: |
Solvent free epoxy coatings, castings,
sealing & laminating. Very good wetting propertise
of glass fiber in laminating applications.
|
|
| |
| 04.05
HARDENER 280 |
| Type |
: |
Modified
aliphatic polyamine |
Viscosity
in Supply at
at 25°C in Poises. |
:
|
20
- 30 |
| Density
g/CM³ |
: |
1.14
- 1.16 |
| Amine
Value mg. KOH/g. |
: |
450
- 500 |
| Amine
eq. wt. |
: |
62
|
| Mixing
ratio with 100 parts of |
| SYNPOL
200 |
: |
30 - 35
|
| SYNPOL
450 XX |
: |
--
|
| Cure
conditions |
: |
16 - 24 hours at 250 |
| Notes |
: |
High reactivity through built-in
accelerator, immunity against carbon dioxide &
low water miscibility of hardener component, suits
for applications under high humidity, even under
water and temperature upto 50
|
|
|
| Next |
| |
| Amino Resins
| Polyamide Resins
| Epoxy Resins, Epoxy Esters & Reactive Diluents |
| Hardeners & Accelerators
| Polyvinyl Butyral Resins
| Acrylic Resins |
| Phenol Formaldehyde Resins
| Ketone Formaldehyde Resins
| Alkyd Resins |
|
| Home |
Profile |
Quality |
R & D |
| Clientele |
Contact Details |
Feedback |
E-mail |
Best viewed in 800X600 Resolution. E-mail : webmaster@wizzotech.com
For copyright & disclaimer site designed & hosted by Wizz O Tech
|
|
|